Quarries
In this section, we would like to show just a small sample of the numerous projects we have carried out, without forgetting any of them, since, larger or smaller, they have all been important to us and are already part of our history.
We currently have 10 quarries located in Spain and Portugal. Aware of the great importance of an adequate selection of the material, from its obtaining in the quarries, using the most modern techniques of extraction, with the seriousness and commitment of always, we can assure the supply of healthy and correctly squared blocks to all our clients.
| Specific weight | 2650 Kg/m3 |
| Absorption | 0,22% |
| Compression resistance | 203 MPa |
| Bending resistance | 11,06 MPa |
| Break module | 12,88 MPa |
| Abrasion resistance | 9,54 ** (ASTM C241) |
| Shock resistance | 44 cm |
| Flexion resistance after accelerated aging | MPa |
| Frost resistance | 0,07 % |
| Specific weight | 2650 Kg/m3 |
| Absorption | 0,22% |
| Compression resistance | 203 MPa |
| Bending resistance | 11,06 MPa |
| Break module | 12,88 MPa |
| Abrasion resistance | 9,54 ** (ASTM C241) |
| Shock resistance | 44 cm |
| Flexion resistance after accelerated aging | MPa |
| Frost resistance | 0,07 % |
| Specific weight | 2640 Kg/m3 |
| Absorption | 0,38% |
| Compression resistance | 111 MPa |
| Bending resistance | 6,50 MPa |
| Break module | 8,45 MPa |
| Abrasion resistance | 5,83 ** (ASTM C241) |
| Shock resistance | 49 cm |
| Flexion resistance after accelerated aging | 5,50 MPa |
| Frost resistance | 0,07 % |
| Specific weight | 2640 Kg/m3 |
| Absorption | 0,38% |
| Compression resistance | 111 MPa |
| Bending resistance | 6,50 MPa |
| Break module | 8,45 MPa |
| Abrasion resistance | 5,83 ** (ASTM C241) |
| Shock resistance | 49 cm |
| Flexion resistance after accelerated aging | 5,50 MPa |
| Frost resistance | 0,07 % |
| Specific weight | 2630 Kg/m3 |
| Absorption | 0,34% |
| Compression resistance | 122 MPa |
| Bending resistance | 6,30 MPa |
| Break module | 8,05 MPa |
| Abrasion resistance | 8,11 ** (ASTM C241) |
| Shock resistance | 51 cm |
| Flexion resistance after accelerated aging | 5,65 MPa |
| Frost resistance | 0,08 % |
| Specific weight | 2630 Kg/m3 |
| Absorption | 0,34% |
| Compression resistance | 122 MPa |
| Bending resistance | 6,30 MPa |
| Break module | 8,05 MPa |
| Abrasion resistance | 8,11 ** (ASTM C241) |
| Shock resistance | 51 cm |
| Flexion resistance after accelerated aging | 5,65 MPa |
| Frost resistance | 0,08 % |
| Specific weight | 2630 Kg/m3 |
| Absorption | 0,42% |
| Compression resistance | 111 MPa |
| Bending resistance | MPa |
| Break module | 9,20 MPa |
| Abrasion resistance | 6,59 ** (ASTM C241) |
| Shock resistance | 49 cm |
| Flexion resistance after accelerated aging | MPa |
| Frost resistance | 0,08 % |
| Specific weight | 2630 Kg/m3 |
| Absorption | 0,42% |
| Compression resistance | 111 MPa |
| Bending resistance | MPa |
| Break module | 9,20 MPa |
| Abrasion resistance | 6,59 ** (ASTM C241) |
| Shock resistance | 49 cm |
| Flexion resistance after accelerated aging | MPa |
| Frost resistance | 0,08 % |
| Specific weight | 2650 Kg/m3 |
| Absorption | 0,17% |
| Compression resistance | 163 MPa |
| Bending resistance | 8,40 MPa |
| Break module | 12,00 MPa |
| Abrasion resistance | 8,03 ** (ASTM C241) |
| Shock resistance | 45 cm |
| Flexion resistance after accelerated aging | 8,40 MPa |
| Frost resistance | 0,07 % |
| Specific weight | 2650 Kg/m3 |
| Absorption | 0,17% |
| Compression resistance | 163 MPa |
| Bending resistance | 8,40 MPa |
| Break module | 12,00 MPa |
| Abrasion resistance | 8,03 ** (ASTM C241) |
| Shock resistance | 45 cm |
| Flexion resistance after accelerated aging | 8,40 MPa |
| Frost resistance | 0,07 % |
| Specific weight | 2640 Kg/m3 |
| Absorption | 0,22% |
| Compression resistance | 123 MPa |
| Bending resistance | 7,60 MPa |
| Break module | 10,90 MPa |
| Abrasion resistance | 10,80 ** (ASTM C241) |
| Shock resistance | 43 cm |
| Flexion resistance after accelerated aging | 7,60 MPa |
| Frost resistance | 0,10 % |
| Specific weight | 2640 Kg/m3 |
| Absorption | 0,22% |
| Compression resistance | 123 MPa |
| Bending resistance | 7,60 MPa |
| Break module | 10,90 MPa |
| Abrasion resistance | 10,80 ** (ASTM C241) |
| Shock resistance | 43 cm |
| Flexion resistance after accelerated aging | 7,60 MPa |
| Frost resistance | 0,10 % |
| Specific weight | 2620 Kg/m3 |
| Absorption | 0,15% |
| Compression resistance | 160 MPa |
| Bending resistance | 9,55 MPa |
| Break module | 11,90 MPa |
| Abrasion resistance | 9,68 ** (ASTM C241) |
| Shock resistance | 41 cm |
| Flexion resistance after accelerated aging | 9,40 MPa |
| Frost resistance | 0,08 % |
| Specific weight | 2620 Kg/m3 |
| Absorption | 0,15% |
| Compression resistance | 160 MPa |
| Bending resistance | 9,55 MPa |
| Break module | 11,90 MPa |
| Abrasion resistance | 9,68 ** (ASTM C241) |
| Shock resistance | 41 cm |
| Flexion resistance after accelerated aging | 9,40 MPa |
| Frost resistance | 0,08 % |
| Specific weight | Kg/m3 |
| Absorption | % |
| Compression resistance | MPa |
| Bending resistance | MPa |
| Break module | MPa |
| Abrasion resistance | ** (ASTM C241) |
| Shock resistance | 55 cm |
| Flexion resistance after accelerated aging | MPa |
| Frost resistance | 0,04 % |
| Specific weight | Kg/m3 |
| Absorption | % |
| Compression resistance | MPa |
| Bending resistance | MPa |
| Break module | MPa |
| Abrasion resistance | ** (ASTM C241) |
| Shock resistance | 55 cm |
| Flexion resistance after accelerated aging | MPa |
| Frost resistance | 0,04 % |
| Specific weight | 2640 Kg/m3 |
| Absorption | 0,32% |
| Compression resistance | 94,50 MPa |
| Bending resistance | 5,65 MPa |
| Break module | 12,10 MPa |
| Abrasion resistance | 8,11 ** (ASTM C241) |
| Shock resistance | 49 cm |
| Flexion resistance after accelerated aging | 5,65 MPa |
| Frost resistance | 0,09 % |
| Specific weight | 2640 Kg/m3 |
| Absorption | 0,32% |
| Compression resistance | 94,50 MPa |
| Bending resistance | 5,65 MPa |
| Break module | 12,10 MPa |
| Abrasion resistance | 8,11 ** (ASTM C241) |
| Shock resistance | 49 cm |
| Flexion resistance after accelerated aging | 5,65 MPa |
| Frost resistance | 0,09 % |
| Specific weight | 2630 Kg/m3 |
| Absorption | 0,16% |
| Compression resistance | 169 MPa |
| Bending resistance | 8,3 MPa |
| Break module | 10,60 MPa |
| Abrasion resistance | 9,98 ** (ASTM C241) |
| Shock resistance | 49 cm |
| Flexion resistance after accelerated aging | 7,5 MPa |
| Frost resistance | 0,05 % |
| Specific weight | 2630 Kg/m3 |
| Absorption | 0,16% |
| Compression resistance | 169 MPa |
| Bending resistance | 8,3 MPa |
| Break module | 10,60 MPa |
| Abrasion resistance | 9,98 ** (ASTM C241) |
| Shock resistance | 49 cm |
| Flexion resistance after accelerated aging | 7,5 MPa |
| Frost resistance | 0,05 % |